1.1211 is a low-alloy, cold-work tool steel commonly referred to as DIN 11211 or AISI 105WCR1.
Chemical Composition:
c (carbon): 095-1.05%
SI (Silicon): 0. max40%
MN (manganese): 040-0.60%
p (phosphorus): 0. max030%
S (sulfur): 0 max030%
CR (chromium): 050-0.80%
w (tungsten): 050-0.80%
Hardness:
Soft annealed:approx. 160 HB (hardness Brinell).
Normalized:170-220 hb。
Quenched and tempered:250-300 hb。
Corresponding grade standards:
DIN Criteria: 11211
AISI SAE standard: 105WCR1
EN standard: There is no explicit EN standard correspondence and is usually used in conjunction with DIN standard.
Features:
Abrasion resistance:1.1211 steel has good wear resistance after proper heat treatment, which is suitable for the manufacture of some tools and parts that require high wear resistance.
Moderate strength and hardness:After different heat treatment processes, moderate strength and hardness can be obtained, making it suitable for the manufacture of cold work tools.
Good machinability:Due to the presence of suitable alloying elements, 1The 1211 performs well in cutting and machining.
Usage:
Cold Work Tools:1.1211 is suitable for the manufacture of cold work tools such as knives, blades, stamping dies, etc.
Knife manufacturing:Due to its moderate hardness and wear resistance, it can be used in the manufacture of some blades and knives.
Engineered Parts:It also has certain applications in the manufacture of engineering parts that require moderate strength and hardness.
Market outlook:1.1211 is a cold work tool steel with moderate properties and is suitable for the manufacture of a wide range of tools and components. The market outlook is affected by the development of manufacturing demand, tool manufacturing, mold manufacturing and other industries. In option 11211, you need to make informed decisions based on the requirements of your application, cost, and manufacturing process.