CUZN37PB1SN1 tin brass wire is an alloy material composed of copper, zinc, lead and tin, and its composition ratio is CUZN37PB1SN1. This alloy material has good mechanical properties and corrosion resistance, so it has a wide range of applications in many fields.
First of all, let's understand the composition of this alloy material. Among them, copper and zinc are the main constituent elements, with 37% copper content and 63% zinc content. Lead and tin are added as alloying elements, each accounting for 1% of the proportion. The ratio of these elements has been carefully designed to give the CUZN37PB1SN1 tin brass wire a unique property.
Secondly, this alloy material has good mechanical properties. Due to the combination of copper and zinc, the alloy has high strength and hardness, as well as good plasticity and toughness. This makes the CUZN37PB1SN1 tin brass wire rod able to withstand large pressure and stress, and is not easy to deform or break.
In addition, the alloy material has excellent corrosion resistance. Due to the presence of copper and zinc, the alloy is highly resistant to many common corrosive media. This allows the CUZN37PB1SN1 tin brass wire to maintain its structural and performance stability in a variety of environments.
Finally, this alloy material has a very wide range of applications. Due to its excellent mechanical properties and corrosion resistance, CUZN37PB1SN1 tin brass wire rod is widely used in shipbuilding, petrochemical, construction, wire and cable and other fields. In these areas, the alloy material can be used to make a variety of products such as pipes, valves, radiators, connectors, and wires.
Grade: CUZN37PB1SN1 tin brass wire
European standard steel grade CW714R
Corresponds to the standard EN 12166-1998
Copper and copper alloys: general copper wires
Classified as copper and copper alloys
Tags: Complex copper-zinc alloy, Complex brass
Density 84 g/cm3
CUZN37PB1SN1 chemical element content (%)
Composition fe ni cu pb sn other total more
Minimum - 59 04 0.5 - zn: margin
The maximum value is 01 0.3 61 1 1 0.2
Other individual or other aggregate chemical compositions include chemical compositions with values not specified in the table. Analysis should only be carried out if it is assumed to be present or in routine analysis, and there are indications that its components will exceed the specified values.
CUZN37PB1SN1 mechanical properties
Diameter Mark Heat treatment or state Tensile strength Yield point Elongation or elongation after break Hardness
d σb σs δ hbw
mm mpa mpa %
0.1≤d≤20 cuzn37pb1sn1-r350 r350 350~450 ≥15(a100)，
18(a11.3)，
20(a)
0.1≤d≤20 cuzn37pb1sn1-h100 h100 hv: 100~130
1.5≤d≤8 cuzn37pb1sn1-r400 r400 ≥400 ≥10(a100)，
13(a11.3)