Z100CDV5 cold work die steel is a high-quality steel that is widely used in the manufacture of various cold work dies. It has excellent wear and corrosion resistance, and is able to maintain stable performance at high and low temperatures. This steel also has excellent hardness and toughness to withstand high levels of pressure and impact.
The advantage of Z100CDV5 cold work die steel is its high hardness and high wear resistance, which makes it ideal for manufacturing cold work dies such as stamping dies, drawing dies, and shearing dies. The hardness of this steel can be adjusted by heat treatment, making it more resistant to wear and durable.
In addition, Z100CDV5 cold work die steel also has good cutting performance and heat treatment process performance. It can easily perform machining operations such as cutting, grinding, and polishing, and the desired mechanical properties can be obtained with a proper heat treatment process.
Overall, Z100CDV5 cold work die steel is a high-quality steel with excellent wear resistance, corrosion resistance, and mechanical properties. It is suitable for the manufacture of various cold work molds and can obtain the best mechanical properties through the appropriate heat treatment process. Its high hardness and toughness allow it to withstand high levels of pressure and impact, thereby extending the service life of the mold. Therefore, Z100CDV5 cold work die steel is an ideal material choice that can help manufacturers improve production efficiency and product quality.
Grade: Z100CDV5 steel for cold work mold
China ISC T21318
Other names: T20503
Corresponds to standard tool steel
tool and mould steels
Categorization of tool steels
Tags: Steel for cold work molds, Alloy steel
Description Characteristics and uses: air quenching steel, with good air quenching characteristics, wear resistance between high carbon oil quenching die steel and high carbon chromium wear-resistant die steel, but its toughness is good, versatility, especially suitable for making both good wear resistance and good toughness molds, such as feeding dies and forming dies, rolls, punches, calendering dies and wire rolling dies.
This standard is applicable to hot rolled, forged, cold-drawn, silver bright bar steel and machined delivery steel of tool and die steel, and its chemical composition is also applicable to ingots, billets and their products
Z100CDV5 chemical element composition content (%)
Composition C Si Mn P s Cr Mo V
The minimum value is 095 - 4.75 0.9 0.15
The maximum value is 105 0.5 1 0.03 0.02 5.5 1.4 0.5
Smelting method: electric arc furnace + vacuum degassing.
Z100CDV5 mechanical properties
Condition: Heat treatment or state hardness
HBW delivery status annealed 255
Specimen quenched HRC
Sample heat treatment system: 790 15 °C preheating, 940 °C (salt bath) or 950 °C (furnace control atmosphere) 6 °C heating, heat preservation 5 15min oil cooling; 200 6 °C tempered once, 2h
Note: The holding time refers to the time that the specimen is held after it reaches the heating temperature.
Note: The specimen is kept for 5 min in a salt bath and 5 15 min in a furnace atmosphere