1. TC4 titanium alloy rod (Ti6Al4V) useAerospace, aviation, navigation, ships, seawater desalination, petroleum, chemical industry, machinery and equipment, nuclear power equipment, power equipment, automobile and motorcycle parts, sports and leisure, medical components, iron and steel and metallurgy, high-tech fields.
2. TC4 titanium alloy rod (Ti6Al4V) processing: titaniumThe indefinite length of the bar is 300-6000mm, the indefinite length of the annealed bar is 300-2000mm, and the length of the fixed length or double length should be within the range of the indefinite length. The allowable deviation of the length of the fixed length is +20mm; The length of the gauge should also be included in the incision amount of the bar, and the amount of each incision is 5mmThe length of the cut-and-length or multiplier should be indicated in the contract. Hot forging - hot rolling - polishing (polishing).
3. TC4 titanium alloy rodTechnical Requirements:
1. The chemical composition of titanium and titanium alloy rods should be in accordance with GB T 36201. When it is necessary to repeatedly test, the allowable deviation of the chemical composition shall be in accordance with GB T 36202.
2. The diameter or side length of the hot-working bar and its allowable deviation shall comply with the provisions of Table 1.
3. After hot processing, the allowable deviation of the diameter of the cold-drawn bar should comply with the industry regulations after turning (grinding) the bar and cold rolling.
4. The roundness of the turning (grinding) bar after hot processing should not be greater than half of its dimensional tolerance.
4. TC4 titanium alloy rodExecutive Standards:
GB 2965-2007, GB T13810, Q BS5331-91
American Standard: ASTM B348, ASTM F136, ASTM F67, AMS4928
Specification: (diameter * length mm): 8mm-250mm*l
Delivery status: hot working state, annealed state.