AISI5130H alloy steel is commonly used in the manufacture of mechanical parts, such as bearings, gears, pins, etc. The following is about the characteristics and application range of AISI5130H alloy steel:
AISI5130H Chemical Composition:
Silicon si: 015～0.35
Manganese mn: 060～0.90
Sulfur s : 0030
Phosphorus p : 0030
Chromium cr: 080～1.10
Nickel ni: 025
Copper cu: 0030
AISI5130H Mechanical Properties:
Tensile strength b (mpa): 885(90).
Yield Strength s (MPa): 685(70).
Elongation δ5 : 11
Section shrinkage 45
Impact power AKV (J): 47
Impact toughness value kv (j cm): 59(6).
Hardness : 187HB
Specimen size: The specimen blank size is 25mm
Feature: High Strength: AISI5130H alloy steel has excellent strength, which is suitable for the manufacture of mechanical parts under high load and high stress environment.
Excellent wear resistance: This alloy steel has good wear resistance, which can effectively resist wear and prolong the service life of parts.
Good heat treatment: AISI5130H alloy steel performs stably during heat treatment, and it is easy to obtain the required hardness and strength.
Scope of application: Bearing manufacturing: AISI5130H alloy steel is often used to manufacture bearings that bear high-speed rotation and high loads to ensure the stable operation of the bearings for a long time.
Gear Manufacturing: Due to its high strength and wear resistance, AISI5130H alloy steel is often used in the manufacture of various types of gears to ensure the reliability and longevity of the transmission system.
Pin Manufacturing: In mechanical systems that need to withstand shock and torque loads, AISI5130H alloy steel is commonly used to manufacture pin shafts to ensure that the connection of parts and components is firm and stable.
To sum up, AISI5130H alloy steel is suitable for manufacturing bearings, gears, pins and other components in mechanical parts, and provides a reliable solution with its high strength, wear resistance and heat treatment properties.