2.0932 high wear-resistant and high-strength aluminum bronze plate and sheet is a metal material with excellent performance, and its unique chemical composition and process treatment make it have the characteristics of high wear resistance and high strength. This kind of aluminum bronze plate and sheet has a wide range of applications, such as in machinery manufacturing, petrochemical industry, aerospace and other fields.
First of all, 20932 high wear resistance and high strength aluminum bronze plate and sheet have very high wear resistance. Because its hardness and strength are very high, it can work stably for a long time under various harsh working conditions, effectively reducing wear and friction, and improving the service life of equipment and tools.
Secondly, 20932 high wear-resistant and high-strength aluminum bronze plates and sheets also have very high strength. It is able to withstand very large pressure and stress, and is not easy to deform or break, ensuring the safety and stability of equipment and tools.
In addition, 2.0932 high wear resistance and high strength aluminum bronze plate and sheet also have good corrosion resistance and high temperature resistance. It can be used for a long time in various environments without rust or oxidation and other problems, and at the same time, it can also withstand the test of high temperatures, ensuring the reliability and stability of equipment and tools.
In short, 20932 high wear resistance and high strength aluminum bronze plate and sheet is a very excellent metal material, which has a wide application prospect in many fields due to its high wear resistance, high strength, corrosion resistance and high temperature resistance. In the future, with the continuous development of science and technology, this kind of aluminum bronze plate and sheet will be used in more fields, bringing more convenience and benefits to people's life and work.
2.0932 high-strength aluminium bronze
Grade: Cu-Al8Fe3
Number: CW303G
Classification: Copper alloys
Density 77 g/cm³
Standard: EN 1653:1998 Copper and copper alloys. Plates, sheets and circles for boilers, pressure vessels and hot water storage devices
EN 1652:1998 Copper and copper alloys. Plates, sheets, strips and rounds for general purpose
EN 12165:1998 Copper and copper alloys. Forged and unwrought blanks
EN 12420:1999 Copper and copper alloys. Forgings
chemical composition % of grade 2.0932
fe si mn ni al pb zn sn others -
1.5 - 3.5 max 0.2 max 1 max 1 6.5 - 8.5 max 0.05 max 0.5 max 0.1 total 0.2 cu - remainder
mechanical properties of grade 2.0932
rm - tensile strength (mpa) (r480) 480
rp0.2 0.2% proof strength (mpa) (r480) 210
a - min. elongation at fracture (%r480) 30
vickers hardness ( hv): h110) 110