GH4169** Form: plates, rods, tubes, steel strips, wires, forgings, forging pipes, forging plates, forging rods, round bars, plates, thin plates, seamless pipes, welded pipes, round bars, wires, steel plates, disc rounds, strips.
1. Introduction. GH4169 is a high-strength, high-toughness nickel-based alloy with good corrosion resistance and high temperature resistance, which is widely used in aerospace, automotive, engineering and marine fields.
Second, performance characteristics.
1.High strength: GH4169 has high tensile strength and yield strength, and can maintain stable performance in high temperature and high pressure environments.
2.High toughness: GH4169 has good toughness and crack resistance, and can resist large shocks and vibrations.
3.Corrosion resistance: GH4169 has good corrosion resistance in acidic, alkaline and salt water, and is not susceptible to corrosion.
4.High temperature resistance: GH4169 has stable performance at high temperatures, and can be used as structural materials and seals in high temperature environments.
5.Abrasion resistance: GH4169 has good anti-wear properties and can be used for wear and friction materials.
3. Use. 1.Aerospace: GH4169 can be used in engine parts, high-temperature bearings and seals in the aerospace field.
2.Automotive Engineering: GH4169 can be used in engine parts, transmission housings and seals in the automotive engineering field.
3.Engineering & Marine: GH4169 can be used in pressure vessels, seals and structural materials in high temperature and high pressure environments in the engineering and marine fields.
Fourth, parameter data.
1.Density: 82 g/cm³
2.Melting Point: 1260-1340
3.Yield strength: approx. 420 MPa
4.Tensile strength: approx. 550 MPa
5.Elongation: about 28%.
6.Salt water corrosion resistance: 100 hours (immersion in 1.)8% NaCl water).
7.Sulfuric acid corrosion resistance: 50 hours (submerged in 1.)4% H2SO4 in water).
8.Hydrofluoric acid corrosion resistance: 10 minutes (immersion in 1.)4% HF water).
V. Conclusions. GH4169 is a nickel-based alloy with good comprehensive properties, with high strength, high toughness and corrosion resistance, suitable for structural materials and seals in aerospace, automotive engineering and shipbuilding. Its excellent properties and stable chemical properties make it an important material choice in high-temperature and high-pressure environments.