Ingredient content:
The chemical composition of N08810 alloy is as follows:
Nickel (Ni): 300% -35.0%
Chromium (cr): 190% -23.0%
Iron (Fe): 005% - Margin.
Carbon (c): 015% -0.1%
Manganese (mn): 015% -1.50%
Silicon (Si): 10%
Sulfur (s): 0015%
Copper (Cu): 075%
Aluminum (AL): 06%
Titanium(Ti): 06%
Performance data: Density: 80 g/cm³
Melting Point: 1350-1400
Mechanical properties (minimum at room temperature):
Tensile strength: 450 n mm
Yield strength: 180 n mm
Elongation: 35%.
1.Definition: N08810 refers to a metal material that can maintain good structure and properties above 800 degrees Celsius. These materials have excellent resistance to heat, corrosion, and oxidation at high temperatures.
2.Features: N08810 has the following features:
a.High melting point: N08810 typically has a high melting point, allowing it to maintain structural stability at high temperatures.
b.Oxidation resistance: N08810 is resistant to oxidation and corrosion, maintaining the performance and service life of the material.
c.Heat resistance: N08810 has good heat resistance and is able to maintain strength and rigidity in high-temperature environments.
d.Low coefficient of expansion: N08810 typically has a low coefficient of thermal expansion, allowing it to maintain a stable size at high temperatures.
Chemical composition (nominal) 002 c、0.50 mn、0.35 si、80.00 ni、4.20 mo、bal。Iron Specification: MIL-N-14411C Ingredient 1, ASTM A-753-78 Density: 874G CM3 applicationHYMU80 is mainly used for the manufacture of transformer cores with winding toroids and laminations to meet compatibility and weight requirements. It is also used as a shield to protect electrical components from stray magnetic fields.