SOMS60 Machined Tin Brass is a special metal material, which is an alloy composed of elements such as copper, tin and zinc. This material has good mechanical properties and corrosion resistance, so it is widely used in various fields, such as construction, chemical industry, shipbuilding and automobile manufacturing.
SOMS60 machined tin brass has high strength and hardness, can withstand large pressure and friction, and at the same time, its plasticity and toughness are also very good, and can be bent, cut and welded. In addition, due to a layer of tin plating on its surface, it also has good corrosion resistance and can be used for a long time in harsh environments.
During the manufacturing process, SOMS60 machining tin brass requires a series of processing treatments, including melting, casting, heat treatment and surface treatment. These treatment steps improve the mechanical properties and corrosion resistance of the material, making it more suitable for a wide range of applications.
Overall, SOMS60 machined tin brass is an excellent metal material, and its high strength, high hardness and good corrosion resistance make it widely used in many fields. In the future, with the continuous progress of technology and the continuous expansion of application scenarios, the application prospect of SOMS60 processed tin brass will be broader.
Grade: SOMS60 machined tin brass
China ISC T46410
Corresponds to standard GB T 5231-2012
Processing of copper and copper alloy grades and chemical compositions
Classified as copper and copper alloys
Performance Weldability
Tags: Tin brass
Note Similar to HSN62-1, the main product is wire.
Welding rods for ship welding structures.
Scope: This standard specifies the grades and chemical compositions of processed copper and copper alloys
This standard applies to copper and copper alloy processed products produced by pressure processing methods and the ingots and billets used
SOMS60 chemical element content (%)
Composition fe cu pb sn other total more
Min - 59 - 1 - zn: margin
The maximum value is 01 61 0.3 1.5 1
Other individual or other aggregate chemical compositions include chemical compositions with values not specified in the table. Analysis should only be carried out if it is assumed to be present or in routine analysis, and there are indications that its components will exceed the specified values.
The iron content of brass for diamagnetic use is 003%。
SOMS60 mechanical properties
Diameter, distance to the opposite edge, marking, heat treatment or state, tensile strength, yield point, elongation or elongation after break, hardness
d/t σb σs δ hbw
mm mpa mpa %
5 soms60-r340 r340 ≥340 ≥140 ≥15(a11.3)，
20(a)
5 soms60-h080 h080 80~120
5 soms60-r400 r400 ≥400 ≥180 ≥10(a11.3)，
15(a)
5 soms60-h105 h105 105~145