NS335 alloy
The solution treatment temperature range of NS335 alloy is 1050 1100, for thicknesses less than 1For 5mm material, it is recommended to use water quenching as the cooling method, but also rapid air cooling can be used to obtain maximum corrosion resistance. During heat treatment, the workpiece must be kept clean. NS335 is widely used in most chemical applications and high-temperature environments.
NS335 is an alloy with excellent corrosion resistance, which is widely used in the chemical industry and high-temperature environments. Solution treatment is a critical step in the manufacturing process, with a temperature range of 1050 to 1100. In this temperature range, the chemical composition of NS335 is fully homogenized and an austenitic structure is formed, thus guaranteeing excellent corrosion resistance.
NS335 chemical element
For thicknesses less than 1For 5mm material, the recommended cooling method is water quenching. This is because water quenching can quickly cool the material, avoiding the phenomenon of coarse grains during the cooling process, and thus obtaining maximum corrosion resistance. Rapid air cooling can also be used as a cooling method.
During heat treatment, the workpiece must be kept clean. Any impurities or contaminants may affect the performance and corrosion resistance of NS335. Therefore, the workpiece needs to be heat treated in a clean environment to avoid any contamination.
In addition to being widely used in the chemical industry, NS335 is also widely used in high-temperature environments. In high-temperature environments, NS335 is still able to maintain excellent corrosion resistance and mechanical properties. This makes NS335 an ideal material for use in high-temperature environments.
In summary, the solution treatment temperature range of NS335 is 1050 1100, for thicknesses less than 1For 5mm material, it is recommended to cool it by water quenching or rapid air cooling. During heat treatment, the workpiece must be kept clean. NS335 has been widely used in the chemical industry and high-temperature environments, and has excellent corrosion resistance and mechanical properties.