Haynes 263 has excellent high temperature strength and creep resistance. At high temperatures, its tensile strength can reach 1400MPa, yield strength can reach 1035MPa, and elongation is 30%. At the same time, the creep resistance of Haynes263 is also very good, and it can maintain stability for a long time.
Antioxidant capacity;
Haynes263 has good oxidation resistance and can be used for a long time in high temperature, high air pressure and strong oxidation environment. At a high temperature of 1000 °C, Haynes263 has a relatively low oxidation rate, which can effectively extend the service life of the material.
Haynes 263 Chemically Typical Nickel: Residual Cobalt: 1900 - 21.00 Chromium: 1900 - 21.00 Molybdenum: 560 - 6.10 Titanium: 19-2.4 titanium + carbon: 004-0.08 Aluminum: 0060 Manganese: 060 Si: 040 iron: 070Boron: 0005 Copper: 020 sulfur: 0007 Silver: 00005 Bismuth: 0Alloy 0001 Haynes 263 has excellent forming and welding properties. The hot working temperature of this alloy ranges from about 1750 to 2150 degrees Fahrenheit (954 to 1177 degrees Celsius). The alloy has excellent ductility in the annealed state, so it can also be formed by cold working. Complex part forming operations may require intermediate annealing in the temperature range of 1900 to 2000 degrees Fahrenheit (1038 to 1093 degrees Celsius). All hot- or cold-worked parts should be annealed and cooled quickly to restore the best balance of performance. Hot rolled coil