CW710R complex brass rod is a high-performance metal material that is widely used in a variety of engineering and manufacturing applications. Due to its excellent mechanical properties and corrosion resistance, it has a wide range of applications in industries such as automotive, marine, oil and gas, chemical and electric power.
The manufacturing process for this complex brass bar is very rigorous and requires multiple processes. First, raw materials such as copper and zinc are precisely blended and then smelted into copper alloys at high temperatures. During the melting process, temperature and time need to be controlled to ensure that the chemical composition and physical properties of the copper alloy are optimal. Next, the copper alloy is processed into bars through a continuous casting and rolling process, and the surface treatment is carried out. These treatments include polishing, brushing, and spraying to improve the appearance quality and corrosion resistance of the bar.
Compared with other metal materials, CW710R complex brass rod has higher strength and hardness, while also having good plasticity and toughness. This allows it to maintain stable performance in environments subjected to high loads and shocks. In addition, this brass rod also has good electrical and thermal conductivity, which can meet various engineering needs.
In addition to its excellent properties, the CW710R complex brass bar is easy to machine and weld. During machining, it can easily perform operations such as cutting, drilling, bending, and straightening. This makes it possible to quickly and efficiently complete a wide range of complex parts and structural parts in the manufacturing process. In addition, this brass bar has good welding properties and can be reliably connected with other metal materials.
Grade: CW710R complex brass bar
European standard steel grade CUZN35Ni3MN2ALPB
Corresponds to EN 12163-2016
Copper & Copper Alloys - General Purpose Bars
copper and copper alloys - rod for general purposes
Classified as copper and copper alloys
Tags: Brass
Density 83 g/cm3
CW710R chemical element composition content (%)
Composition: fe si, mn, ni, cu, pb, al sn, other, total, more
Minimum - 15 2 58 0.2 0.3 - zn: margin
The maximum value is 05 0.1 2.5 3 60 0.8 1.3 0.5 0.3
Other individual or other aggregate chemical compositions include chemical compositions with values not specified in the table. Analysis should only be carried out if it is assumed to be present or in routine analysis, and there are indications that its composition will exceed the specified value.
CW710R mechanical properties
Diameter, distance to the opposite edge, marking, heat treatment or state, tensile strength, yield point, elongation or elongation after break, hardness
d/t σb σs δ hbw
mm mpa mpa %
5 cw710r-r490 r490 ≥490 ≥290 ≥15(a11.3)，
18(a)