CUZN30 brass spring band connector is a commonly used metal connector, which is made of CUZN30 brass with good elasticity and conductivity. It is widely used in various electronic devices to connect lines and components to ensure the stable transmission of current.
The CUZN30 brass spring band connector is compact and easy to install and remove. It is designed with a spring band that can be tightly wrapped around wires or cables, providing a reliable connection. Due to its excellent elasticity and durability, the connector is able to withstand multiple mating and unplugging without being easily damaged.
In addition, the material of CUZN30 brass spring band connector is stable, with good oxidation resistance and corrosion resistance. It can be used in a variety of harsh environmental conditions, such as high temperature, low temperature, humidity, etc., to ensure the reliability and stability of the connection.
When using the CUZN30 brass spring belt connector, the following points should be noted: First, make sure that the connector matches the size of the wire or cable to avoid being too tight or too loose;Secondly, it should be installed and removed according to the prescribed operating procedures to avoid damage to the connector or wire;Finally, the condition of the connector should be checked regularly, and if it is found loose or damaged, it should be repaired or replaced in time.
Grade: CUZN30 Brass Spring Strip for connectors
European standard steel grade CW505L
Corresponds to the standard EN 1654-1998
Copper and copper alloys. Strips for springs and connectors
copper and copper alloys - strip for springs and connectors
Classified as copper and copper alloys
Tags: copper-zinc alloy, brass
Description Modulus of elasticity: 115 gpa
Density 85 g/cm3
CUZN30 chemical element content (%)
Composition: Fe Ni Cu Pb al Sn Other Total More
Min - 69 - zn: Margin
The maximum value is 005 0.3 71 0.05 0.02 0.1 0.1
Other individual or other aggregate chemical compositions include chemical compositions with values not specified in the table. Analysis should only be carried out if it is assumed to be present or in routine analysis, and there are indications that its components will exceed the specified values.
CUZN30 mechanical properties
Condition Tags Heat treatment or state Tensile strength Yield point Elongation or elongation after break Hardness
b σs δ hbw
mpa mpa %
Strip CUZN30-R350 R350 350 430 (170) 21;25ⓑ
Strip CUZN30-H095 H095 HV: 95 125
Strip CUZN30-R410 R410 410 490 9;12ⓑ
Strip CUZN30-H120 H120 HV: 120 155
Strip CUZN30-Y350 Y350 350 (440) 9;12ⓑ
Strip CUZN30-R480 R480 480 560 4;6ⓑ
Strip CUZN30-H150 H150 HV: 150 180
Strip CUZN30-Y460 Y460 460 (540) 4;6ⓑ
Strip CUZN30-R550 R550 550 640 2
Strip CUZN30-H170 H170 HV: 170 200
Strip CUZN30-Y530 Y530 530 (620) 2
Strip CUZN30-R630 R630 630
Strip CUZN30-H190 H190 HV: 190