2.0261 brass extruded rod is a high-quality brass product with good mechanical properties and corrosion resistance. This bar is made by an extrusion process, so it has a smooth surface, high dimensional accuracy, and good mechanical properties. In occasions that require high strength and corrosion resistance, such as construction, chemical industry, shipbuilding and other fields, 20261 brass extruded rod is a very practical material.
In addition, 2.0261 brass extruded rod also has good electrical and thermal conductivity, so it is also widely used in the electrical and electronics industry. Due to its excellent processing properties, this bar can also be made into various complex parts and components through various processing processes. During the manufacturing process, 20261 brass extruded rods require heat treatment and surface treatment to ensure their best performance and appearance.
Overall, 2.0261 brass extruded rod is a high-quality, high-performance material with a wide range of application prospects. Its emergence has provided strong support for the development of various industries, and promoted the progress of technology and the development of industries. In the future, with the continuous development of science and technology, 2The application field of 0261 brass extruded rod will be further expanded, bringing more convenience and benefits to human production and life.
The above is for 2A detailed introduction of 0261 brass extruded rod, including its manufacturing process, performance characteristics, application fields, etc. Through these introductions, we can understand the importance and advantages of this material, and provide us with reference and guidance for practical applications.
grade : 2.0261 brass extruded rod
number: cuzn28
Classification: Copper-zinc alloy
Standard: EN 12163:1998 Copper and copper alloys. Universal rod
Description Features and Applications:
It is very easy to cold form through deep drawing, pressing, riveting, flanging, very easy to weld, and easy to plating on steel.
It is used for radiators, musical instruments, various deep-drawn parts, leaf springs, and spring parts for connectors
chemical composition % of grade cuzn28 ( 2.0261)
fe ni al cu pb sn others -
max 0.05 max 0.3 max 0.02 71 - 73 max 0.05 max 0.1 total 0.1 zn - remainder
mechanical properties of grade cuzn28 ( 2.0261)
rm - tensile strength (mpa) (r310) 310
rm - tensile strength (mpa) (r370) 370
rp0.2 0.2% proof strength (mpa) (r310) 120
rp0.2 0.2% proof strength (mpa) (r370) 320
a - min. elongation at fracture (%r310) 27
a - min. elongation at fracture (%r370) 10
brinell hardness (hb): h085) 85 - 115
brinell hardness (hb): h115) 115 - 145