00Cr22Ni5Mo3N is a stainless steel material, and its chemical composition is as follows:1Carbon (C) content: about 003% 2.Chromium (CR) content: approx. 22% 3Nickel (Ni) content: about 5% 4Molybdenum (Mo) content: about 3% 5Nitrogen (N) content: The specific content depends on the specific standard.
Mechanical properties usually include the following aspects:1Tensile strength: generally between about 650 MPa and 850 MPa, 2Yield strength: generally between about 250 MPa and 450 MPa, 3Elongation: Typically between about 25% and 35%, it exhibits good ductility and is suitable for some applications that require bending or stamping. 4.Hardness: Usually between about 180 HB and 220 HB, the physical properties usually include the following:1Density: about 78 g/cm³， 2.Thermal conductivity: generally between about 14 W (m·k) and 16 W (M·K), 3Coefficient of linear expansion: typically between about 16 10 (-6) °C and 18 10 (-6) °C, 4Magnetism: Typically low magnetism, which may be a necessary feature in some applications.
Common processing methods include:1Including cold rolling, cold drawing, cold stamping, etc., suitable for the production of thin plates, filaments and precision parts, etc. 2.Hot rolling, hot extrusion, etc., suitable for the production of thick plates, bars and profiles, etc. 3.The internal structure and properties of the material can be improved through the forging process, which is suitable for the production of high-strength and high-plasticity parts. 4.Machining methods such as turning, milling, and drilling are suitable for precision machining and forming of materials.
Applications:1It is used in the production of corrosion-resistant equipment and parts such as vessels, pipelines, reactors, etc. 2.It is used in the manufacture of seawater treatment equipment, offshore platform structure, etc., and has good seawater corrosion resistance. 3.It is used in the production of food processing equipment, brewing equipment, etc., and the materials are required to be non-toxic, tasteless and will not have any effect on food. 4.Used in the manufacture of surgical instruments, artificial joints, etc., the material is required to have good biocompatibility and corrosion resistance. 5.Used in the manufacture of energy equipment and pipelines such as oil and natural gas, the material is required to have good high temperature resistance and corrosion resistance.