CW504L brass extruded rod is a high-quality brass product that is widely used in various industrial fields because of its excellent mechanical properties and corrosion resistance. This bar is extruded using an advanced extrusion process, which ensures its dense structure and uniform component distribution. In appearance, it presents a unique golden-yellow luster, giving it a noble and elegant feel.
The chemical composition of CW504L brass extruded rod has been carefully formulated so that it has a good balance between hardness and toughness. This bar has high strength and hardness and is able to withstand heavy loads and complex stress conditions. At the same time, it also has good ductility and plasticity, which is easy to process and shape. This makes it highly flexible and adaptable in the manufacturing process, able to meet a wide range of different application needs.
In addition to excellent mechanical properties, CW504L brass extruded rods also have good corrosion resistance. It maintains stable performance in a wide range of environments and is not susceptible to corrosion and oxidation. This makes it have a wide range of application prospects in marine engineering, chemical equipment, construction and other fields. In addition, it has good electrical and thermal conductivity to meet the needs of the electrical and electronics industry.
In conclusion, CW504L brass extruded rod is a high-quality brass product with excellent mechanical properties, corrosion resistance and good processing properties. Its wide range of applications has proven its superior performance and reliability in a variety of different fields. Whether for industrial production or for high-end decoration, it is an invaluable material choice.
Grade : CW504L Brass Extruded Rod
number: cuzn28
Classification: Copper-zinc alloy
Standard: EN 12163:1998 Copper and copper alloys. Universal rod
Description Features and Applications:
It is very easy to cold form through deep drawing, pressing, riveting, flanging, very easy to weld, and easy to plating on steel.
It is used for radiators, musical instruments, various deep-drawn parts, leaf springs, and spring parts for connectors
chemical composition % of grade cuzn28 ( cw504l )
fe ni al cu pb sn others -
max 0.05 max 0.3 max 0.02 71 - 73 max 0.05 max 0.1 total 0.1 zn - remainder
mechanical properties of grade cuzn28 ( cw504l )
rm - tensile strength (mpa) (r310) 310
rm - tensile strength (mpa) (r370) 370
rp0.2 0.2% proof strength (mpa) (r310) 120
rp0.2 0.2% proof strength (mpa) (r370) 320
a - min. elongation at fracture (%r310) 27
a - min. elongation at fracture (%r370) 10
brinell hardness (hb): h085) 85 - 115
brinell hardness (hb): h115) 115 - 145