SOMS58Al2 manganese aluminum brass bar is a high-performance metal material that is widely used in various engineering fields due to its excellent mechanical properties and corrosion resistance.
First of all, SOMS58AL2 manganese aluminum brass bar has excellent strength and hardness, which means that it is able to withstand high loads and stresses, so as to maintain stable performance in various harsh environments. Secondly, the material also has excellent corrosion resistance, and can be used for a long time in various corrosive media such as acids and alkali salts, thereby greatly extending the service life of engineering facilities.
In addition, SOMS58AL2 manganese aluminum brass bar also has good processing performance and welding performance, which can be easily used for cutting, bending, drilling and welding, thereby simplifying the process flow of engineering manufacturing. At the same time, the material is also easy to carry out surface treatment, such as galvanizing, spraying, etc., to further improve its corrosion resistance and aesthetics.
In terms of application, SOMS58AL2 manganese aluminum brass bar is mainly used in the manufacture of various pipelines, valves, pump bodies, ships, chemical equipment, etc., especially in marine engineering, petrochemical, pharmaceutical and other fields. Due to its excellent performance and reliability, the material has become one of the materials of choice for many important projects.
Grade: SOMS58AL2 manganese aluminum brass bar
European standard steel grade CUZN40AL2
Other names: UH-12
Corresponds to the standard EN 12164-2016
Easy-to-machine copper and copper alloy bars
copper and copper alloys — rod for free machining purposes
Classified as copper and copper alloys
Tags: Complex Brass, Aluminum Brass
Description Features:
Good abrasion resistance; Excellent corrosion resistance; Strength; Excellent hot forging performance; Good cutting performance; Excellent self-lubricating properties.
Usage: bearings, wear plates, propulsion shafts, bushings.
Density 81 g/cm3
SOMS58AL2 chemical element composition content (%)
Composition: fe si, mn, ni, cu, pb, al sn, other, total, more
Minimum - 03 1.5 - 57 0.2 1.3 - zn: margin
Maximum value 1 13 3 1 59 0.8 2.3 0.4 0.3
Other individual or other aggregate chemical compositions include chemical compositions with values not specified in the table. Analysis should only be carried out if it is assumed to be present or in routine analysis, and there are indications that its composition will exceed the specified value.
SOMS58AL2 mechanical properties
Diameter Mark Heat treatment or state Tensile strength Yield point Elongation or elongation after break Hardness
d σb σs δ hbw
mm mpa mpa %
5≤d≤80 soms58al2-r540 r540 ≥540 ≥280 ≥15 -
5≤d≤80 soms58al2-h130 h130 - 130~170
5≤d≤50 soms58al2-r590 r590 ≥590 ≥370 ≥10 -